Portable Digital Coating Thickness Gauge TIME®2600 adopts two thickness-measuring methods: magnetic induction (ferrous) and eddy current (non-ferrous). Coating Thickness Gauge TIME2601, ferrous and non-ferrous eddy current coating painting thickness. https://timetech-ndt.com/product/coating-thickness-gauge-time2600/
It can rapidly, nondestructively, and precisely measure the thickness of non-magnetic coating on magnetic metal substrate, and the thickness of non-conductive coating on non-magnetic metal substrate.
This paint meter can be equipped with 6 optional probes for different applications. It is suitable for both field testing and laboratory research. Coating Thickness Gauge TIME2601, ferrous and non-ferrous eddy current coating painting thickness.
Features
● Two operation principles are adapted: magnetic induction (ferrous) and eddy current (non-ferrous) to take non-destructive measurements
● 6 types of probes are available for different applications
● Features two working modes: DIRECT and BATCH& two measuring ways: CONTINUE and SINGLE
● Statistics include the mean, maximum, minimum, test numbers and standard deviation.
● Memory of 640 data
● Two calibration methods for better correction
● Integrated with printer to print the statists values if needed
● Low battery indication and error alarm
● Backlight for the screen
● Auto or manual shutdown
● Conform to the standards of DIN, ISO, ASTMBS.
Probe types
F
N
Measuring methods
magnetic induction
eddy current
Measuring range
0 ~1250 μm
0 ~1250 μm, 0 to 40μm (for chrome plate on copper)
Minimum resolution
0.1μm
Tolerance
Zero point calibration
±(3%H+1)μm
± (3%H+1.5)μm
H means the thickness of tested piece
Two points calibration
±[(1~3)%H+1]μm
±[(1~3)%H+1.5]μm
H means the thickness of tested piece
Measuring condition
Min. curvature radius (mm)
Convexity 1.5
Convexity 3
Min. testing area diameter (mm)
Ø7
Ø5
Critical thickness of substrate(mm)
0.5
0.3
Standards DIN,ISO,ASTM,BS
Calibration Zero and foil calibration
Interface RS232
Statistic Number of measurement, mean, standarddeviation, maximum and minimum
Data memory 640 readings
Limits Adjustable with alarm
Power NiMH rechargeable battery
Operating environment
Temperature: 0~40℃
Humidity: 20%~90%
No strong magnetic field
Dimensions (mm) 230×86×47
Optional Probes and Application Guide
Probe model
F400
F1
F1/90º
F10
N1
CN02
Operating principle
Magnetic induction
Eddy current
Measuring range (µm)
0-400
0-1250
0-10000
0 to 1250 μm
0 to 40μm
(for chrome plate
on copper)
10~200
Low range resolution (µm)
0.1
0.1
10
0.1
1
Accuracy
One-point calibration (µm)
±(3%H+1)
±(3%H+10)
±(3%H+1.5)
±(3%H+1)
Two-point calibration (µm)
±[(1~3)H%+0.7]
±[(1~3)H%+1]
±[(1~3)%H+10]
±[(1~3)%H+1.5]
Measuring conditions
Min curvature of the min area (mm)
Convex 1
1.5
Flatten
10
3
Flatten
Diameter of the min area (mm)
φ3
φ7
φ7
φ40
φ5
φ7
Critical thickness of substrate (mm)
0.2
0.5
0.5
2
0.3
unlimited
Standard Delivery
Main unit 1
Probe 1
Substrate 1
Calibration foil 1
Charger 1
Printing paper 1
TIME certificate 1
Warranty card 1
Instruction manual